BOILER & PRESSURE VESSEL QUALITY STEEL PLATES
| Specification |
Chemical |
Mechanical Mpa, min |
C
Max |
Mn
Max |
Si
Max |
S
Max |
P
Max |
CE
|
Tensile
Min |
Yield
Min |
% EL
50 GL |
Min
200 GL |
Bend |
Impact |
ASTM-A 515
Gr - 60
Gr - 70 |
|
| 0.22 |
0.90 |
0.15
0.40 |
0.035 |
0.035 |
--- |
415
550 |
220 |
25 |
21 |
1.5T |
--- |
| 0.31 |
1.20 |
0.15
0.40 |
0.035 |
0.035 |
--- |
485
620 |
260 |
21 |
17 |
2T |
--- |
ASTM-A 516
Gr - 60
Gr - 70 |
|
| 0.23 |
0.85
1.2 |
0.15
0.40 |
0.04 |
0.035
|
0.42 |
415
550 |
220 |
25 |
21 |
1.5T |
-46°C / 18J |
| 0.28 |
0.85
1.2 |
0.15
0.40 |
0.04 |
0.035 |
0.43 |
485
620 |
260 |
21 |
17 |
2T |
-46°C / 20J |
IS 2002 Gr - I
&
DIN 17155 Gr - H1 |
0.18 |
0.50
1.20 |
0.15
0.35 |
0.04 |
0.035 |
0.44 |
360
480 |
235 |
24 |
--- |
2T |
--- |
IS 2002 Gr - II
&
DIN 17155 Gr - H2 |
0.02 |
0.50
1.20 |
0.15
0.35 |
0.04 |
0.035 |
0.44 |
410
530 |
265 |
22 |
--- |
2T |
---- |
IS 2002 Gr - III
&
DIN 17155 Gr - H3 |
0.22 |
0.50
1.20 |
0.15
0.35 |
0.04 |
0.035 |
0.44 |
460
580 |
290 |
21 |
--- |
3T |
--- |
| ASTM A 283 Gr C |
0.28 |
0.90 |
0.17
0.35 |
0.04 |
0.035 |
--- |
380
515 |
205 |
25 |
22 |
2T |
--- |
| ASTM A 285 Gr C |
0.28 |
0.90 |
0.17
0.35 |
0.04 |
0.035 |
--- |
380
515 |
205 |
27 |
23 |
1.5T |
--- |
| ASTM A 537 CI-I |
0.24 |
0.7
1.6 |
0.15
0.50 |
0.035 |
0.035 |
0.45 |
485
620 |
345 |
22 |
18 |
2T |
-30OC / 20J |
| ASTM A 572 Gr-65 |
0.23 |
1.65 |
0.40 |
0.05 |
0.04 |
--- |
550 |
450 |
17 |
15 |
--- |
---- |
| ASTM A 573 Gr-50 |
0.25 |
1.40 |
0.40 |
0.05 |
0.04 |
--- |
485
620 |
260 |
--- |
18 |
--- |
--- |
| EN 10028 |
|
|
|
|
|
|
|
|
|
|
|
|
| P235 GH |
0.16 |
0.40
1.20
|
0.35 |
0.025 |
0.030 |
--- |
360
480
|
235 |
25 |
--- |
--- |
Impact 0C / 27J |
| P265 GH |
0.20 |
0.30
1.4
|
0.17
0.35 |
0.025 |
0.030 |
--- |
410
530
|
265 |
23 |
--- |
--- |
0C / 27J |
| P275 GH |
0.20 |
0.80
1.5
|
0.35 |
0.025 |
0.030 |
--- |
430
550
|
275 |
22 |
--- |
--- |
0C / 27J |
| P355 GH |
0.22 |
1.0
1.7
|
0.60 |
0.025 |
0.030 |
--- |
510
650
|
355 |
21 |
--- |
--- |
0C / 27J |
| API 5L |
|
|
|
|
|
|
|
|
|
|
|
|
| X 52 |
0.28 |
1.40 |
--- |
0.030 |
0.030 |
--- |
455
758
|
359
531
|
--- |
--- |
--- |
--- |
| X 56 |
0.26 |
1.40 |
--- |
0.030 |
0.030 |
--- |
490
758
|
386
544
|
--- |
--- |
--- |
--- |
| X 60 |
0.26
|
1.40
|
--- |
0.030 |
0.030 |
--- |
517
758
|
414
565
|
--- |
--- |
--- |
--- |
| X 65 |
0.26 |
1.45 |
--- |
0.030 |
0.030 |
--- |
531
758
|
448
600
|
--- |
--- |
--- |
--- |
| X 70 |
0.23
|
1.60
|
--- |
0.030 |
0.030 |
--- |
565
|
482
|
--- |
--- |
--- |
--- |
| List of certified steel of EN 10025+A1; the certification made by the Technical Inspection Body TUV Nord e.V. according to National Standards of European Inion states (Ilyich Iron and Steel Works) |
| |
| European Standard EN 10025+A1 (1993) |
EN 10025:1990 |
Germany
DIN 17100 |
France
NF A35-501 |
England BS 4360 |
Spain
36080-90 UNE |
Italy
EN10025 UNJ |
Belgium EN10025 NBN |
Sweden XXXX-XX SS |
Portugal EN 10025 |
Austria EN10025 ONORM |
Norway
XX XXX NS |
| Grade of steel |
Number material |
| S235JRG2
S235JO
S235J2G3
S235J2G3 |
1.0038
1.0114
1.0116
1.0117 |
Fe360 BFN
Fe360 C
Fe360 D1
Fe360 D2 |
RSt37-2
St37-3U
St37-3N |
E 24-3
E 24-4
|
40B
40C
40D |
AE 235B-FN
AE 235 C
AE 235 D |
Fe360 C
Fe360 D
|
AE 235-C
AE 235-D
|
t312-00 |
Fe360-C
Fe360-D
|
RSt 360 B
St 360 C
St 360 CE
St 360 D |
NS 12 123
NS 12 124
NS 12 124 |
| S275JR
S275JO
S275J2G3
S275J2G4 |
1.0044
1.0143
1.0144
1.0145 |
Fe430 B
Fe430 C
Fe430 D1
Fe430 D2 |
St44-2
St44-3 U
St44-3N |
E 28-2
E 28-3
E 28-4 |
43B
43C
43D |
AE 275 B
AE 275 C
AE 275 D |
Fe430 B
Fe430 C
Fe430 D |
AE 255-B
AE 255-C
AE 255-D |
14 12-00
14 14-00
14 14-01 |
Fe430-B
Fe430-C
Fe430-D |
St 430 B
St 430 C
St 430 CE
St 430 D |
NS 12 142
NS 12 143
NS 12 143 |
| S355JR
S355JO
S355J2G3
S355J2G4
S355K2G3 |
1.0045
1.0553
1.0570
1.0577
1.0595 |
Fe510 B
Fe510 C
Fe510 D1
Fe510 D2
Fe510 DD1 |
St52-3U
St52-3N
|
E 36-2
E 36-3
E 36-4 |
50B
50C
50D
50DD |
AE 355 B
AE 355 C
AE 355 D |
Fe510-B
Fe510-C
Fe510-D |
AE 355-B
AE 355-C
AE 355-D
AE 355-DD |
|
Fe510-B
Fe510-C
Fe510-D
Fe510-DD |
St 510 C
St 510 D
|
NS 12 153
NS 12 153
|
|
|
| |
|
| |
|
| |
Technical characteristics of plates of 8-30 mm thickness made of structural carbon steel according to European Standard EN 10025 +A1 (DIN 17100) (Ilyich Iron and Steel Works). |
| |
| Standard number |
EN 10025+A1
DIN 17100 |
Grade of steel EN 10025
DIN 17100 |
S235JRG2
RSt37-2 |
S235JO |
S235J2G3
St37-3 |
S235J2G4 |
S275JR
St44-2 |
S275JO |
S275J2G3
St44-3 |
S275J2G4 |
S355JR |
S355JO |
S355J2G3
St52-3 |
S355J2G4 |
S355K2G3 |
| Name of elements |
Chemical composition of steel
Element mass share, % |
C
Mn
Si
P
S
Al (general)
N |
<=0,17
<=1,40
-
<=0,045
<=0,045
-
<=0,009 |
<=0,17
<=1,40
-
<=0,040
<=0,040
-
<=0,009 |
<=0,17
<=1,40
-
<=0,035
<=0,035
>=0,020
- |
<=0,17
<=1,40
-
<=0,035
<=0,035
>=0,020
- |
<=0,21
<=1,50
-
<=0,045
<=0,045
-
<=0,009 |
<=0,18
<=1,50
-
<=0,040
<=0,040
-
<=0,009 |
<=0,18
<=1,50
-
<=0,035
<=0,035
>=0,020
- |
<=0,18
<=1,50
-
<=0,035
<=0,035
>=0,020
- |
<=0,24
<=1,60
<=0,55
<=0,045
<=0,045
-
- |
<=0,20
<=1,60
<=0,55
<=0,040
<=0,040
-
- |
<=0,20
<=1,60
<=0,55
<=0,035
<=0,035
>=0,035
- |
<=0,20
<=1,60
<=0,55
<=0,035
<=0,035
>=0,020
- |
<=0,20
<=1,60
<=0,55
<=0,035
<=0,035
>=0,020
- |
| C equivalent |
<=0,35 |
<=0,40 |
<=0,45 |
| Name of characteristics |
Mechanical properties
Values of characteristics |
Yield point
R eN , N/mm2
S <= 16 mm
S > 16 mm |
>=235
>=225 |
>=275
>=265 |
>=355
>=345 |
| Tensile strength Rm, N/mm2 |
340-470 |
410-560 |
490-630 |
Elongation at rupture
A, % (Lo=5,65 So )
longitudinal
transverse |
>=26
>=24 |
>=22
>=20 |
>=21
>=19 |
Impact work KV
(according to Sharpy),
J
+20oC
0oC
-20oC |
>=27
-
- |
-
>=27
- |
-
-
>=27 |
-
-
>=27 |
>=27
-
- |
-
>=27
- |
-
-
>=27 |
-
-
>=27 |
>=27
-
- |
-
>=27
- |
-
-
>=27 |
-
-
>=27 |
-
-
>=40 |
|
|
| |
|
| |
|
| |
Technical characteristics of certified boiler and shipbuilding steel of 8-30 mm thickness (Ilyich Iron and Steel Works). |
| |
| Kind of product |
Boiler (heat resistant) steel |
Shipbuilding steel |
| Standard number |
EN 10028-2 (DIN 17155) |
Lloyd's Register (UK), ABS (USA), requirements |
| Grade of steel |
P235GH
(H l ) |
P265GH
(H l l ) |
P295GH
(17Mn4) |
P355GH
(19Mn6) |
A |
B |
D |
AH32 |
DH32 |
AH36 |
DH36 |
| Chemical composition of steel |
| Name of elements |
Element mass share, % |
Mn
Si
P
S
Al (general)
A (dissolved)
Cr
Cu
Ni
Mo
Ti
V
Nb |
<=0,16
0,40-1,20
<=0,35
<=0,030
<=0,025
>=0,020
-
<=0,30
<=0,30
<=0,30
<=0,08
<=0,03
<=0,02
<=0,010 |
<=0,20
0,50-1,40
<=0,40
<=0,030
<=0,025
>=0,020
-
<=0,30
<=0,30
<=0,30
<=0,08
<=0,03
<=0,02
<=0,010 |
0,08-0,20
0,90-1,50
<=0,40
<=0,030
<=0,025
>=0,020
-
<=0,30
<=0,30
<=0,30
<=0,08
<=0,03
<=0,02
<=0,010 |
0,10-0,22
1,0-1,70
<=0,60
<=0,030
<=0,025
>=0,020
-
<=0,30
<=0,30
<=0,30
<=0,08
<=0,03
<=0,02
<=0,010 |
<=0,21
>=2,5xCmin
<=0,50
<=0,035
<=0,035
-
-
-
-
-
-
-
-
- |
<=0,21
<=0,60
0,10-0,35
<=0,035
<=0,035
-
-
-
-
-
-
-
-
- |
<=0,18
<=0,60
0,10-0,35
<=0,035
<=0,035
>=0,020
>=0,015
-
-
-
-
-
-
- |
<=0,18
0,9-1,6
0,10-0,50
<=0,035
<=0,030
>=0,020
>=0,015
<=0,20
<=0,35
<=0,40
<=0,08
<=0,02
(0,05-0,10) *
(0,02-0,05) * |
<=0,18
0,9-1,6
0,10-0,50
<=0,035
<=0,030
>=0,020
>=0,015
<=0,20
<=0,35
<=0,40
<=0,08
<=0,02
(0,05-0,10) *
(0,02-0,05) * |
<=0,18
0,9-1,6
0,10-0,50
<=0,035
<=0,030
>=0,020
>=0,015
<=0,20
<=0,35
<=0,40
<=0,08
<=0,02
(0,05-0,10) *
(0,02-0,05) * |
<=0,18
0,9-1,6
0,10-0,50
<=0,035
<=0,030
>=0,020
>=0,015
<=0,20
<=0,35
<=0,40
<=0,08
<=0,02
(0,05-0,10) *
(0,02-0,05) * |
| C equivalent |
|
<=0,40 |
<=0,40 |
<=0,40 |
To be approved |
| Mechanical properties |
| Name of characteristics |
Values of characteristics |
ReN, N/mm2 S<=16 mm
S>16 mm2 |
>=235
>=225 |
>=265
>=255 |
>=295
>=290 |
>=355
>=345 |
>=235 |
>= 315 |
>= 355 |
| Rm, N/mm2 |
360-480 |
410-530 |
460-580 |
510-650 |
440-490 ( 400-520)** |
440-590 |
490-620 |
| A, % (Lo=5,65(So) ? ) |
>=25 |
>=23 |
>=22 |
>=21 |
>=22 |
>=22 |
>=21 |
| Impact work (according to Sharpy), J |
at 0o C |
|
0oC |
-20oC |
0oC |
-20oC |
0oC |
-20oC |
| >= 27 |
>= 27 |
>= 27 |
>= 27 |
- |
>= 27 |
>= 27 |
>= 34 |
>= 34 |
>= 34 |
>= 34 |
Re 0,2% , N/mm2
+300oC
+400oC |
>= 130
>= 110 |
>= 155
>= 130 |
>= 185
>= 155 |
>= 215
>= 180 |
-
- |
-
- |
-
- |
-
- |
-
- |
-
- |
-
- |
|
|
| |
* To be approved
** ABS (USA) requirements |
| |
|
| |
Table #2. Basic chemical composition of the steel smelted by the Ilyich Works and used for production of the rolled stock (Ilyich Iron and Steel Works). |
| |
| Grade of steel |
Content of elements, % |
| C |
Mn |
Si |
Cr |
Ni |
Cu |
Al |
S |
P |
| not more than |
| Carbon steel of common quality - GOST 380 |
St1kp
Ct1ps
Ct1sp
St2kp
St2ps
St2sp
St3kp
St3ps
St3sp |
0,06-0,12
0,06-0,12
0,06-0,12
0,09-0,15
0,09-0,15
0,09-0,15
0,14-0,22
0,14-0,22
0,14-0,22 |
0,25-0,50
0,25-0,50
0,25-0,50
0,25-0,70
0,25-0,70
0,25-0,70
0,30-0,80
0,40-0,85
0,40-0,85 |
<=0,05
0,05-0,15
0,15-0,30
<=0,05
0,05-0,15
0,15-0,30
<=0,05
0,05-0,15
0,15-0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
-
-
-
-
-
-
-
-
- |
0,050
0,050
0,050
0,050
0,050
0,050
0,050
0,050
0,050 |
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040 |
| Carbon steel of common quality - GOST 380 |
St3Gps
St3Gsp
St4sp
St5ps
St5sp |
0,14-0,22
0,14-0,20
0,18-0,27
0,28-0,37
0,28-0,37 |
0,80-1,10
0,80-1,10
0,40-0,70
0,50-1,00
0,50-1,00 |
<=0,15
0,15-0,30
0,15-0,30
0,05-0,15
0,15-0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
-
-
-
-
- |
0,050
0,050
0,050
0,050
0,050 |
0,040
0,040
0,040
0,040
0,040 |
| Structural high-grade carbon steel - GOST 1050 |
08kp
08p
08
10kp
10ps
10
15kp
15ps
15 |
0,05-0,12
0,05-0,11
0,05-0,12
0,07-0,14
0,07-0,14
0,07-0,14
0,12-0,19
0,12-0,19
0,12-0,19 |
0,25-0,50
0,35-0,65
0,35-0,65
0,25-0,50
0,35-0,65
0,35-0,65
0,25-0,50
0,35-0,65
0,35-0,65 |
<=0,03
0,05-0,17
0,17-0,37
<=0,07
0,05-0,17
0,17-0,37
<=0,07
0,05-0,17
0,17-0,37 |
<=0,10
<=0,10
<=0,10
<=0,15
<=0,15
<=0,15
<=0,25
<=0,25
<=0,25 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
-
-
-
-
-
-
-
-
- |
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040 |
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035 |
| Structural high-grade carbon steel - GOST 1050 |
20kp
20ps
20
25
30
40
45 |
0,17-0,24
0,17-0,24
0,17-0,24
0,22-0,30
0,27-0,35
0,37-0,45
0,42-0,50 |
0,25-0,50
0,35-0,65
0,35-0,65
0,50-0,80
0,50-0,80
0,50-0,80
0,50-0,80 |
<=0,07
0,05-0,17
0,17-0,37
0,17-0,37
0,17-0,37
0,17-0,37
0,17-0,37 |
<=0,25
<=0,25
<=0,25
<=0,25
<=0,25
<=0,25
<=0,25 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30 |
-
-
-
-
-
-
- |
0,040
0,040
0,040
0,040
0,040
0,040
0,040 |
0,035
0,035
0,035
0,035
0,035
0,035
0,035 |
| Low carbon high-grade steel for cold stamping - GOST 9045 |
08U
08kp
08ps |
<=0,07
<=0,10
<=0,09 |
0,20-0,35
0,20-0,40
0,20-0,45 |
<=0,01
<=0,03
<=0,04 |
<=0,03
<=0,10
<=0,10 |
<=0,06
<=0,10
<=0,10 |
<=0,06
<=0,15
<=0,15 |
0,02-0,07
-
- |
0,025
0,030
0,030 |
0,020
0,025
0,025 |
| Structural high-grade carbon steel for cold stamping - GOST 4041 |
| 08UA |
<=0,10 |
0,20-0,40 |
<=0,03 |
<=0,10 |
<=0,15 |
<=0,20 |
0,02-0,08 |
0,025 |
0,020 |
| Low alloyed steel - GOST 19281 |
9G2S
09G2
09G2D
12GS
16GS
17GS
17G1S
14G2
10G2S1
10G2S1D
10XSND |
<=0,12
<=0,12
<=0,12
0,09-0,15
0,12-0,18
0,14-0,20
0,15-0,20
0,12-0,18
<=0,12
<=0,12
<=0,12 |
1,3-1,7
1,4-1,8
1,4-1,8
0,8-1,2
0,9-1,2
1,0-1,4
1,15-1,6
1,2-1,6
1,3-1,65
1,3-1,65
0,5-0,8 |
0,5-0,8
0,17-0,37
0,17-0,37
0,5-0,8
0,4-0,7
0,4-0,6
0,4-0,6
0,17-0,37
0,8-1,1
0,8-1,1
0,8-1,1 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
0,6-0,9 |
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
0,5-0,8 |
<=0,30
<=0,30
0,15-0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
<=0,30
0,15-0,30
0,4-0,6 |
<=0,05
-
-
-
-
-
-
-
-
-
- |
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040
0,040 |
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035
0,035 |
| Steel for shipbuilding - GOST 5521 |
A
V
A32
D32
A36
D36 |
<=0,21
<=0,21
<=0,21
<=0,18
<=0,18
<=0,18
<=0,18 |
0,6-1,0
0,6-1,1
0,6-1,4
0,9-1,6
0,9-1,6
0,9-1,6
0,9-1,6 |
0,15-0,35
0,15-0,35
0,15-0,35
0,15-0,50
0,15-0,50
0,15-0,50
0,15-0,50 |
<=0,30
<=0,30
<=0,30
<=0,20
<=0,20
<=0,20
<=0,20 |
<=0,30
<=0,30
<=0,30
<=0,40
<=0,40
<=0,40
<=0,40 |
<=0,30
<=0,30
<=0,30
<=0,35
<=0,35
<=0,35
<=0,35 |
-
<=0,06
0,015-0,06
0,015-0,06
0,015-0,06
<=0,06
0,015-0,06 |
0,035
0,035
0,035
0,035
0,035
0,035
0,035 |
0,035
0,035
0,035
0,035
0,035
0,035
0,035 |
|
|
Inspection & Approval Certificates : C/W Certificate (Calibration Works Certificate) EN10204 3.1 Mill Test Certificate, NACE MR-0175 / ISO 15156, European Pressure Equipment Directive PED-97/23/EC, AD-2000-WO, ASME Boiler & Pressure Vessel Code Sec.II Part A Ed. 2008, API 6A, with 3.2 certificate duly Certified & Approved by LRS (Lloyd's Register), GL (Germanischer Lloyd), BV (Bureau Veritas), DNV (Det Norske Veritas), SGS, TUV, ABS, RINA, IRS, NORSOK Approved
If you have any requirement of above items, please feel free to contact us
Regards,
CONTACT PERSON :
MUKESH SHAH
Director
Mobile No. 0091 - 9820292499
Email - marketing@rolexmetals.com
ROLEX METAL DISTRIBUTORS
( A METAL & STEEL Company )
57-A, KHATARGALLI,
THAKURDWAR,
MUMBAI - 400002, INDIA.
TEL.No. 0091-22-23858802
TEL.No. 0091-22-23823963
FAX No. 0091-22-23898724
Email - marketing@rolexmetals.com
Website – www.rolexmetals.com
CHAIRMAN – chairman@rolexmetals.com MANAGING DIRECTOR – managingdirector@rolexmetals.com TECHNICAL DIRECTOR – technicaldirector@rolexmetals.com SALES DIRECTOR – salesdirector@rolexmetals.com COMMERCIAL DIRECTOR – commercialdirector@rolexmetals.com COMMERCIAL MANAGER – commercial@rolexmetals.com GENERAL MANAGER – generalmanager@rolexmetals.com SALES MANAGER – salesmanager@rolexmetals.com PURCHASE MANAGER – purchasemanager@rolexmetals.com TECHNICAL MANAGER – technical@rolexmetals.com WORKS MANAGER – worksmanager@rolexmetals.com STORES MANAGER – stores@rolexmetals.com WAREHOUSE MANAGER – warehouse@rolexmetals.com SALES DOMESTIC – salesdomestic@rolexmetals.com SALES INTERNATIONAL – salesinternational@rolexmetals.com SALES GENERAL – sales@rolexmetals.com PURCHASE GENERAL – purchase@rolexmetals.com FINANCE MANAGER – finance@rolexmetals.com ACCOUNTS MANAGER – accounts@rolexmetals.com GENERAL INFORMATION – info@rolexmetals.com EXPORT MANAGER – export@rolexmetals.com IMPORT MANAGER – import@rolexmetals.com AIR EXPORT – airexport@rolexmetals.com SEA EXPORT – seaexport@rolexmetals.com CUSTOMS – customs@rolexmetals.com AIR FREIGHT – airfreight@rolexmetals.com SEA FREIGHT – seafreight@rolexmetals.com DESPATCH – despatch@rolexmetals.com INSPECTION – inspection@rolexmetals.com LOGISTICS – logistics@rolexmetals.com TRANSPORT – transport@rolexmetals.com KALAMBOLI WAREHOUSE – kalamboli@rolexmetals.com TALOJA WAREHOUSE – taloja@rolexmetals.com KHOPOLI WAREHOUSE – khopoli@rolexmetals.com NHAVA SHEVA WAREHOUSE – nhavasheva@rolexmetals.com KANDLA WAREHOUSE – kandla@rolexmetals.com MUMBAI WAREHOUSE – mumbai@rolexmetals.com STOCKYARD – stockyard@rolexmetals.com SERVICE – service@rolexmetals.com SUPPORT – support@rolexmetals.com RECRUITMENT – career@rolexmetals.com WEBMASTER – webmaster@rolexmetals.com CUSTOMER CARE – customercare@rolexmetals.com
|
|